Appearance外觀

Clear powder清粉狀

Solids (%)固含

>99

Tg (ºC)玻璃化溫度

60

Epoxy equivalent weight (g/mol)環氧當量

445

Plastic塑料

Application用於

Recommended Dosage推薦用量

(% w/w)

Polyesters (PET)聚酯

Fiber (staple and filament)

纖維（短纤维和长丝）

0.1 to 0.7

Injection/blow molding bottle

注塑/吹塑瓶

0.1 to 0.8

Sheet, tape and profile extrusion

片材，胶带和型材挤出

0.2 to 1.0

Film and bottle blow molding

薄膜和瓶吹塑

0.2 to 1.0

Strapping打包帶

0.2 to 1.0

Compatibilization PET/PA-nylon

聚酯與尼龍相容

0.4 to 1.5

Foam發泡

0.4 to 1.5

Polyesters (PETG, PBT, PLA, others)

聚酯（PETG，PBT，PLA，其他）

Injection Molding注射成型

0.1 to 0.3

Fiber纖維

0.1 to 0.7

Profile extrusion型材擠出

0.2 to 1.0

Sheet and film片材和薄膜

0.2 to 1.0

Branching分枝

0.5 to 1.5

Foam發泡

0.4 to 1.5

Polyamides (nylon, PA 6, other)

聚酰胺（尼龙，PA 6，其他）

Injection Molding注射成型

0.1 to 0.3

Profile extrusion型材擠出

0.4 to 1.0

Sheet, film and tape

片材，薄膜，胶带

0.4 to 1.5

Branching分枝

0.5 to 1.5

Compatibilization polyester/PA-nylon

增容聚酯/ PA尼龍

0.5 to 1.5

Polycarbonates (PC)

聚碳酸酯（PC）

Injection molding注射成型

0.1 to 0.3

Hydrolytic stabilization水解穩定

0.4 to 1.5

Sheet and film片材和薄膜

0.4 to 1.5

Branching分枝

0.5 to 1.5

Other condensation thermoplastics (TPU, POM)

其他冷凝熱塑性塑料（TPU，POM）

Melt strength熔體強度

0.3 to 1.0

Stabilization穩定

0.2 to 1.0

Operation操作

Procedure步驟 

1. Dry blending

     幹混

1. Flake or masterbatch can be dry-blended with pre-dried and cold (<40°C) plastic pellets or flakes with the aid of a low shear mixer such as a tumble mixer or conical mixer.

 可以使用低剪切混合器（如滚筒式混合器或锥形混合器）将片状或母料与预干燥和冷（<40°C）塑料颗粒或薄片干混

2. THYOSIL CXP5045 can be mixed with other materials in a high shear mixer below 50°C.

 可以在低於50℃的高剪切混合器中与其他材料混合。

2. Addition of THYOSIL CXP5045 on a single screw extruder, twin screw extruder or kneader

在單螺桿擠出機，双螺杆挤出机或knea上添加THYOSIL CXP 5045

1. Dry-blend prepared as in (1) can be volumetrically, gravimetrically or flood fed directly into mixing zone of the extruder   

      如（1）中制备的干混物可以体积计量，重量分析或直接进料到挤出机的混合区

2. Gravimetric feed metering systems can be used to feed flake or masterbatch product form in a parallel stream with the plastic directly into the feeding zone of the extruder. Belt and disc feeders are particularly recommended.

Twin-Screw Feeders Non intermeshing spiral screw with 6mm clearance between the screw and the tube recommended. Eliminate agglomeration at the throat or feed zone by maintaining tube temperature below 80°C.

重量進料計量系統可用於將平行流中的薄片或母粒產品形式直接進入擠出機的進料區。 特别推荐皮带和圆盘给料机。

雙螺桿給料機推薦使用螺桿和管之間6mm間隙的非齧合螺旋螺桿。 通过保持管温度低于80℃消除在喉部或进料区聚集

3. Volumetric Feeders: well calibrated feeders with variation of less than 0,5% are recommended. Clearance of 3 to 5 mm between the screw and tube is also required to reduce fines. Eliminate agglomeration at the throat or feed zone by maintaining tube temperature below 80°C

.體積給料機：建议使用良好校准的变送量小于0.5％的进料器。 螺杆和管之间的间隙为3至5毫米也需要減少細粉。 通过保持管温度低于80℃消除在喉部或进料区聚集。

4. Side feed systems and other types of forced dosing extruders may be employed with all solid product forms, except for fine powder, to feed the products downstream. Residence time recommendations are given below in reference to downstream feeds.

除了細粉末之外，侧进料系统和其它类型的强制加料挤出机可以与所有固体产品形式一起使用，以在下游进料产品。 以下参考下游饲料给出停留时间建议。

5. Direct gravimetric/volumetric addition of the chain extender in any form to the plastic melt may be carried out through any suitable downstream venting or degassing port.

任何形式的擴鏈劑直接重量/體積添加到塑料熔體可以通過任何合適的下游排氣口或脫氣口進行。

3. Addition during injection molding and combined injection-blow molding operations

在注塑成型和組合注塑吹塑成型操作期間添加

1. Dry-blends prepared as in (1) can be volumetrically, gravimetrically or flood fed directly into the mixing zone of the injection molder.如（1）中制备的干混合物可以体积计量，重量分析或直接进料到注射成型机的混合区域

2. Flakes not recommended for direct addition to injection molding equipment.片狀不建議直接加入注塑設備。

3. Separate gravimetric feed metering systems can be used to feed masterbatches of THYOSIL CXP5045 in a parallel stream with the plastic directly into the feeding zone of the injection molder. Belt and disk feeders are particularly recommended.

Twin-Screw no intermeshing spiral screw with 6mm clearance between the screw and the tube recommended.

單獨的重量計量計量系統可用於將THYOSIL CXP5045的母料與塑料直接進入注射成型機的進料區。 特别推荐皮带和圆盘给料机。

雙螺桿無齧合螺旋螺釘，螺杆和管之间6mm間隙推薦。

4. Volumetric Feeders: Well calibrated feeders with variation of less than 0,5% are recommended, Clearance of 3 to 5 mm between the screw and tube is also required to reduce fines. Eliminate agglomeration at the throat or feed zone by maintaining temperatures below 100°C for MB polymer carriers or 80°C for wax carriers.

體積給料機：建议使用良好校准的变送量小于0.5％的进料器，螺杆和管之间的间隙为3至5 mm也需要減少細粉。 通过将MB聚合物載體的溫度保持在低於100℃，对蜡载体保持温度低于80℃，可消除喉部或进料区的附聚。

Operation操作

Procedure步驟

Pre-drying

預乾燥

Pre-dry the base plastic at manufacturer’s recommended conditions.

推薦下預乾燥基礎塑料。

In some instances small amounts of THYOSIL CXP5045 can be compensated for poor or incomplete drying, thus bringing robustness and saving to your operations.

在某些情況下，添加少量的THYOSIL CXP5045可以補償不良或不完全的乾燥，从而为您的操作带来方便和節省操作。

Hygroscopicity: there is no evidence of bulk absorption of moisture over extended periods of time for THYOSIL CXP5045.

At normal conditions of temperature and relative humidity its surface reaches equilibrium saturation through adsorption at less than 0,25% of moisture.

At extreme conditions its surface reaches equilibrium saturation at less than 0,50% of moisture.

This means that THYOSIL CXP5045 can generally be processed without any drying, even after long exposure to drastic conditions bringing no more than 5ppm moisture per every 0,1% used.

吸溼性：THYOSIL CXP5045在長時間內沒有大量吸收水分的跡象。在正常的温度和相对湿度条件下，其表面通过吸附小于0.25％的水分达到平衡饱和度。

在極端條件下其表面水分，在小于0.50％达到平衡饱和。这意味着即使经过长时间暴露于剧烈的条件下，THYOSIL CXP5045通常也可以進行加工處理，每0.1％使用不超过5ppm的水分。

Ins systems where moisture sensitivity is extreme, THYOSIL CXP5045 can be dried in a desiccant dryer ant 30°C for 1 hour, prior to use.

在潮溼敏感度極高的系統中，THYOSIL CXP5045可以在乾燥劑乾燥器中於30℃ 乾燥1小時，然后再使用。

Extruder/injection molder temperature profile

擠出機/注塑機溫度曲線

Where feeding solid THYOSIL CXP5045 in any solid form, except masterbatch, into the first zone of the extruder or infection molder, we recommend to operate this zone at 20°C to 40 °C lower temperature than normal. This will prevent early melting and agglomeration of the additive.

在將固體形式除母粒之外的固體THYOSIL CXP5045進入擠出機或感染模塑機的第一區域內，建议比常温低 ，在20℃至40℃的温度下操作该区域。 这将防止添加剂的早期熔化和附聚。

All other zones should employ normal processing condition as recommended by the plastic’s manufacturer.

所有其他區域應採用塑料製造商推薦的正常加工條件。

Additive thermal stability

添加劑熱穩定性

THYOSIL CXP5045 is thermally stable up to 320°C. Above this temperature additive decomposition may occur.

THYOSIL CXP5045在320°C以下是熱穩定的。 高于此温度可能会发生分解。

Residence time

停留時間

THYOSIL CXP5045 reacts quickly. Its reaction will be over 99% complete if at least 3 min residence time is provided at 200°C in a well-mixed system. Alternatively, 45 sec residence time at 280°C will provide 99% completion.

THYOSIL CXP5045快速反應。 如果在200℃下在充分混合的系统中至少提供3分鐘的停留時間，其反应将达到99％以上。 或者，在280℃下停留时间为45秒將完成99％。

These limits accommodate most extrusion and injection molding processed for the recommended thermoplastics and applications.

這些限制適用於爲推薦的熱塑性塑料和應用而加工的大多數擠出和注塑。

For use in polymerization reactors where residence time is over 5 minutes, see recommendations in section “Methods of Dosage”.

用於停留時間超過5分鐘的聚合反應釜中，请参见“剂量方法”一节中的建议。

Extrude variable

拉伸變量

PET Control控制

0,50%

THYOSIL CXP5045

1,00% THYOSIL CXP5045

1,50% THYOSIL CXP5045

Pressure die壓模

1

1.25-1.45

1.55-1.80

1.80-2.00

Pressure screen

壓力篩

1

1.25-1.45

1.90-1.80

1.80-2.00

Motor power draw

電機功率

1

1.05-1.08

1.13-1.12

1.12-1.15

Extrude variable

拉伸變量

Steady feed within 5% of target value

穩定飼料在目標值的5％以内

Steady feed within 10% of target value

穩定飼料在目標值的10％以内

Steady feed within 20% of target value

穩定飼料在目標值的20％以内

Pressure die壓模

± 2.0%

±4.3%

±9.0%

Pressure screen

壓力篩

±2.5%

±4.5%

±9.2%

Pressure draw壓差

±0.4%

±0.8%

±1.75%

Appearance外觀

Clear powder清粉狀

Solids (%)固含

>99

Tg (ºC)玻璃化溫度

60

Epoxy equivalent weight (g/mol)環氧當量

445

Plastic塑料

Application用於

Recommended Dosage推薦用量

(% w/w)

Polyesters (PET)聚酯

Fiber (staple and filament)

纖維（短纤维和长丝）

0.1 to 0.7

Injection/blow molding bottle

注塑/吹塑瓶

0.1 to 0.8

Sheet, tape and profile extrusion

片材，胶带和型材挤出

0.2 to 1.0

Film and bottle blow molding

薄膜和瓶吹塑

0.2 to 1.0

Strapping打包帶

0.2 to 1.0

Compatibilization PET/PA-nylon

聚酯與尼龍相容

0.4 to 1.5

Foam發泡

0.4 to 1.5

Polyesters (PETG, PBT, PLA, others)

聚酯（PETG，PBT，PLA，其他）

Injection Molding注射成型

0.1 to 0.3

Fiber纖維

0.1 to 0.7

Profile extrusion型材擠出

0.2 to 1.0

Sheet and film片材和薄膜

0.2 to 1.0

Branching分枝

0.5 to 1.5

Foam發泡

0.4 to 1.5

Polyamides (nylon, PA 6, other)

聚酰胺（尼龙，PA 6，其他）

Injection Molding注射成型

0.1 to 0.3

Profile extrusion型材擠出

0.4 to 1.0

Sheet, film and tape

片材，薄膜，胶带

0.4 to 1.5

Branching分枝

0.5 to 1.5

Compatibilization polyester/PA-nylon

增容聚酯/ PA尼龍

0.5 to 1.5

Polycarbonates (PC)

聚碳酸酯（PC）

Injection molding注射成型

0.1 to 0.3

Hydrolytic stabilization水解穩定

0.4 to 1.5

Sheet and film片材和薄膜

0.4 to 1.5

Branching分枝

0.5 to 1.5

Other condensation thermoplastics (TPU, POM)

其他冷凝熱塑性塑料（TPU，POM）

Melt strength熔體強度

0.3 to 1.0

Stabilization穩定

0.2 to 1.0

Operation操作

Procedure步驟 

1. Dry blending

     幹混

1. Flake or masterbatch can be dry-blended with pre-dried and cold (<40°C) plastic pellets or flakes with the aid of a low shear mixer such as a tumble mixer or conical mixer.

 可以使用低剪切混合器（如滚筒式混合器或锥形混合器）将片状或母料与预干燥和冷（<40°C）塑料颗粒或薄片干混

2. THYOSIL CXP5045 can be mixed with other materials in a high shear mixer below 50°C.

 可以在低於50℃的高剪切混合器中与其他材料混合。

2. Addition of THYOSIL CXP5045 on a single screw extruder, twin screw extruder or kneader

在單螺桿擠出機，双螺杆挤出机或knea上添加THYOSIL CXP 5045

1. Dry-blend prepared as in (1) can be volumetrically, gravimetrically or flood fed directly into mixing zone of the extruder   

      如（1）中制备的干混物可以体积计量，重量分析或直接进料到挤出机的混合区

2. Gravimetric feed metering systems can be used to feed flake or masterbatch product form in a parallel stream with the plastic directly into the feeding zone of the extruder. Belt and disc feeders are particularly recommended.

Twin-Screw Feeders Non intermeshing spiral screw with 6mm clearance between the screw and the tube recommended. Eliminate agglomeration at the throat or feed zone by maintaining tube temperature below 80°C.

重量進料計量系統可用於將平行流中的薄片或母粒產品形式直接進入擠出機的進料區。 特别推荐皮带和圆盘给料机。

雙螺桿給料機推薦使用螺桿和管之間6mm間隙的非齧合螺旋螺桿。 通过保持管温度低于80℃消除在喉部或进料区聚集

3. Volumetric Feeders: well calibrated feeders with variation of less than 0,5% are recommended. Clearance of 3 to 5 mm between the screw and tube is also required to reduce fines. Eliminate agglomeration at the throat or feed zone by maintaining tube temperature below 80°C

.體積給料機：建议使用良好校准的变送量小于0.5％的进料器。 螺杆和管之间的间隙为3至5毫米也需要減少細粉。 通过保持管温度低于80℃消除在喉部或进料区聚集。

4. Side feed systems and other types of forced dosing extruders may be employed with all solid product forms, except for fine powder, to feed the products downstream. Residence time recommendations are given below in reference to downstream feeds.

除了細粉末之外，侧进料系统和其它类型的强制加料挤出机可以与所有固体产品形式一起使用，以在下游进料产品。 以下参考下游饲料给出停留时间建议。

5. Direct gravimetric/volumetric addition of the chain extender in any form to the plastic melt may be carried out through any suitable downstream venting or degassing port.

任何形式的擴鏈劑直接重量/體積添加到塑料熔體可以通過任何合適的下游排氣口或脫氣口進行。

3. Addition during injection molding and combined injection-blow molding operations

在注塑成型和組合注塑吹塑成型操作期間添加

1. Dry-blends prepared as in (1) can be volumetrically, gravimetrically or flood fed directly into the mixing zone of the injection molder.如（1）中制备的干混合物可以体积计量，重量分析或直接进料到注射成型机的混合区域

2. Flakes not recommended for direct addition to injection molding equipment.片狀不建議直接加入注塑設備。

3. Separate gravimetric feed metering systems can be used to feed masterbatches of THYOSIL CXP5045 in a parallel stream with the plastic directly into the feeding zone of the injection molder. Belt and disk feeders are particularly recommended.

Twin-Screw no intermeshing spiral screw with 6mm clearance between the screw and the tube recommended.

單獨的重量計量計量系統可用於將THYOSIL CXP5045的母料與塑料直接進入注射成型機的進料區。 特别推荐皮带和圆盘给料机。

雙螺桿無齧合螺旋螺釘，螺杆和管之间6mm間隙推薦。

4. Volumetric Feeders: Well calibrated feeders with variation of less than 0,5% are recommended, Clearance of 3 to 5 mm between the screw and tube is also required to reduce fines. Eliminate agglomeration at the throat or feed zone by maintaining temperatures below 100°C for MB polymer carriers or 80°C for wax carriers.

體積給料機：建议使用良好校准的变送量小于0.5％的进料器，螺杆和管之间的间隙为3至5 mm也需要減少細粉。 通过将MB聚合物載體的溫度保持在低於100℃，对蜡载体保持温度低于80℃，可消除喉部或进料区的附聚。

Operation操作

Procedure步驟

Pre-drying

預乾燥

Pre-dry the base plastic at manufacturer’s recommended conditions.

推薦下預乾燥基礎塑料。

In some instances small amounts of THYOSIL CXP5045 can be compensated for poor or incomplete drying, thus bringing robustness and saving to your operations.

在某些情況下，添加少量的THYOSIL CXP5045可以補償不良或不完全的乾燥，从而为您的操作带来方便和節省操作。

Hygroscopicity: there is no evidence of bulk absorption of moisture over extended periods of time for THYOSIL CXP5045.

At normal conditions of temperature and relative humidity its surface reaches equilibrium saturation through adsorption at less than 0,25% of moisture.

At extreme conditions its surface reaches equilibrium saturation at less than 0,50% of moisture.

This means that THYOSIL CXP5045 can generally be processed without any drying, even after long exposure to drastic conditions bringing no more than 5ppm moisture per every 0,1% used.

吸溼性：THYOSIL CXP5045在長時間內沒有大量吸收水分的跡象。在正常的温度和相对湿度条件下，其表面通过吸附小于0.25％的水分达到平衡饱和度。

在極端條件下其表面水分，在小于0.50％达到平衡饱和。这意味着即使经过长时间暴露于剧烈的条件下，THYOSIL CXP5045通常也可以進行加工處理，每0.1％使用不超过5ppm的水分。

Ins systems where moisture sensitivity is extreme, THYOSIL CXP5045 can be dried in a desiccant dryer ant 30°C for 1 hour, prior to use.

在潮溼敏感度極高的系統中，THYOSIL CXP5045可以在乾燥劑乾燥器中於30℃ 乾燥1小時，然后再使用。

Extruder/injection molder temperature profile

擠出機/注塑機溫度曲線

Where feeding solid THYOSIL CXP5045 in any solid form, except masterbatch, into the first zone of the extruder or infection molder, we recommend to operate this zone at 20°C to 40 °C lower temperature than normal. This will prevent early melting and agglomeration of the additive.

在將固體形式除母粒之外的固體THYOSIL CXP5045進入擠出機或感染模塑機的第一區域內，建议比常温低 ，在20℃至40℃的温度下操作该区域。 这将防止添加剂的早期熔化和附聚。

All other zones should employ normal processing condition as recommended by the plastic’s manufacturer.

所有其他區域應採用塑料製造商推薦的正常加工條件。

Additive thermal stability

添加劑熱穩定性

THYOSIL CXP5045 is thermally stable up to 320°C. Above this temperature additive decomposition may occur.

THYOSIL CXP5045在320°C以下是熱穩定的。 高于此温度可能会发生分解。

Residence time

停留時間

THYOSIL CXP5045 reacts quickly. Its reaction will be over 99% complete if at least 3 min residence time is provided at 200°C in a well-mixed system. Alternatively, 45 sec residence time at 280°C will provide 99% completion.

THYOSIL CXP5045快速反應。 如果在200℃下在充分混合的系统中至少提供3分鐘的停留時間，其反应将达到99％以上。 或者，在280℃下停留时间为45秒將完成99％。

These limits accommodate most extrusion and injection molding processed for the recommended thermoplastics and applications.

這些限制適用於爲推薦的熱塑性塑料和應用而加工的大多數擠出和注塑。

For use in polymerization reactors where residence time is over 5 minutes, see recommendations in section “Methods of Dosage”.

用於停留時間超過5分鐘的聚合反應釜中，请参见“剂量方法”一节中的建议。

Extrude variable

拉伸變量

PET Control控制

0,50%

THYOSIL CXP5045

1,00% THYOSIL CXP5045

1,50% THYOSIL CXP5045

Pressure die壓模

1

1.25-1.45

1.55-1.80

1.80-2.00

Pressure screen

壓力篩

1

1.25-1.45

1.90-1.80

1.80-2.00

Motor power draw

電機功率

1

1.05-1.08

1.13-1.12

1.12-1.15

Extrude variable

拉伸變量

Steady feed within 5% of target value

穩定飼料在目標值的5％以内

Steady feed within 10% of target value

穩定飼料在目標值的10％以内

Steady feed within 20% of target value

穩定飼料在目標值的20％以内

Pressure die壓模

± 2.0%

±4.3%

±9.0%

Pressure screen

壓力篩

±2.5%

±4.5%

±9.2%

Pressure draw壓差

±0.4%

±0.8%

±1.75%